Overview
| brand | Platinum research | Product name | Conductive silver slurry High temperature silver slurry |
| type | Electromagnetic shielding high conductivity material | characteristic | Good adhesion at high and low temperatures, strong resistance and weldability |
| material quality | Silver pine resin diluent | purpose | Class II ceramic capacitors, NTC, piezoelectric ceramic electrodes |
| model | YB-1045 | quantity | five thousand |
| encapsulation | Drum | Batch number | twenty million two hundred and eleven thousand and thirteen |
Product Details
XJY-Ag-80 Series High Temperature Silver Paste
Used as a Class II ceramic capacitor, NTC, and piezoelectric ceramic electrode. Can be burned and has good adhesion.
Main performance indicators:
Product grade
Solid content%
*1 fineness μ M
*2 viscosity Pa. s
PC-Ag-8055
fifty-eight+two
≤ 12
100-300
PC-Ag-8060
sixty-three+two
≤ 12
100-300
PC-Ag-8065
sixty-eight+two
≤ 12
100-300
*When customers request special anti stick requirements, the fineness can be relaxed to 15 μ M
*2. Viscosity testing conditions, BROOK FIELD DV-52 # axis 250.5r/min
Recommended usage conditions:
1. Mixing:Stir well before use.
2. Recommended printing thickness: 10-15 µ m
3. Mesh material and mesh size: Nylon mesh British 200~280 mesh
Stainless steel wire mesh British 200~280 mesh
4. Drying: After printing, place it in a 150-250 ℃ oven or under an infrared light for 2-5 minutes.
5. Sintering process (recommended): Sintering in a tunnel furnace, with a peak sintering temperature of 830+20 ℃, peak insulation time 10-15 minutes, sintering cycle 45-60 minutes.
Performance indicators after firing:
1. Solderability: Excellent (welding conditions Sn/Pb/Ag or Sn/Pb 230 ℃, 1-2 seconds, immersion)
2. Adhesion (2X2mm2, vertical):>40N
3. Square resistance (m Ω/□): 2-4
matters needing attention
1. Safe use: If swallowed, inhaled, or in contact with the skin, the slurry is harmful. Therefore, after use, it should be thoroughly washed with water immediately, avoiding contact with eyes, skin, or clothing, and not near sparks or combustibles. Because it is flammable, it should be tightly covered when not in use to avoid inhaling volatile gases, and air circulation should be maintained during use.
2. This slurry is a ready-to-use product and does not need to be diluted. If dilution is needed, please use our company's diluent to dilute. The amount added should not exceed 3% by weight. Excessive diluent will directly affect the performance of the slurry.
3. The thickness of the printed circuit itself cannot be less than 4 μ m. Otherwise, the conductivity is unstable.
4. This slurry should be stored between 4~25 ℃ in a cool and dry place.
5. Storage period: The original packaging is sealed for six months.