Overview
| brand | Asahi Kasei, Japan | Product characteristics | High mobility |
| Imported or not | no | Manufacturer (place of origin) | Asahi Kasei, Japan |
| Grade | 100Z | Sales method | Brand distribution |
| Processing level | Injection grade | Property level | Flame retardant grade, standard grade, hydrolysis resistant |
| Usage level | Automotive components, electronic and electrical components, home appliance components, and power tool accessories | Product specifications | 25kg |
| proportion | one point zero nine | Shrinkage rate - Flow | 0.50 to 0.80% |
| Water absorption rate | About 0.06% | Forming temperature | 280-330 degrees |
| Modification molding temperature | 260-285 degrees | Performance characteristics | Good dimensional stability |
| Characteristic 1 | Solubility resistance | Characteristic 2 | Good electrical performance |
| Characteristic 3 | Low contractility | Saleable land | nationwide |
| type | Standard material | ?? | nine hundred and ninety-nine |
Product Details
High flow PPO Japan Asahi Kasei 100Z flame-retardant V0 high-strength polyphenylene ether injection grade
Physical Property Table
Performance characteristics
Good dimensional stability
Rigid, high
Solubility resistance
Good electrical performance
Heat resistance, high
Low contractility
Flame retardant performance
Purpose
Electrical/Electronic Applications
Electrical components
Processing
Injection molding
Physical performance
Rated value
Unit system
Testing
Specific gravity
1.09
G/cm& Amp; Sup3< Br/>
ASTM D792
Shrinkage rate flow
0.50 to 0.80
%
ASTM D955
Forming performance
1. Non crystalline material with low moisture absorption< Br/>
2. Poor fluidity, similar to Newtonian fluid, the viscosity is sensitive to temperature, and the product thickness is generally more than 0.8mm. Extremely easy to decompose, producing corrosive gases during decomposition. The molding temperature should be strictly controlled, the mold should be heated, and the pouring system should have low resistance to material flow< Br/>
3. The water absorption rate of polyphenylene ether is very low by about 0.06%, but a small amount of water can cause the surface of the product to appear unsmooth phenomena such as silver threads. It is for drying treatment, and the temperature should not be higher than 150 degrees, otherwise the color will change< Br/>
4. The molding temperature of polyphenylene ether is 280-330 degrees Celsius, modified