Overview
| brand | Saudi QAMAR | type | Standard material |
| producing area | Saudi Arabia | Product name | FD21HN |
| Imported or not | no | Article number | AL-645917303132 |
| Grade | FD21HN | Processing level | Blow molding grade |
| Property level | Transparency level | Usage level | Film grade, universal grade |
| Sales method | Brand distribution | Manufacturer (place of origin) | Saudi QAMAR |
Product Details
Product parameters
| Performance Items | Test conditions [status] | test method | test data | Data unit | ||
| Basic performance | Melt flow rate | ASTM D-1238 | two | G/10min | ||
| density | ASTM D-1505 | zero point nine one eight | G/cm3 | |||
| Mechanical properties | surface hardness | ASTM D-2240 | fifty-four | Shore D | ||
| Tensile strength fracture point | JIS K-6760 | twenty-six | MPa | |||
| tear strength | MD | ASTM D-1922 | thirty | N/mm | ||
| TD | ASTM D-1922 | one hundred and forty | N/mm | |||
| Across Flow | JIS K-6760 | nine hundred | % | |||
| Across Flow | MD | JIS Z 1702 | six hundred | % | ||
| TD | JIS Z 1702 | nine hundred | % | |||
| Yield point of tensile strength | JIS K-6760 | twelve | MPa | |||
| Stretch film quantity | MD | ISO IR 1184 | one hundred and ninety | MPa | ||
| TD | ISO IR 1184 | two hundred and ten | MPa | |||
| Impact strength | ASTM D-1709 | one hundred and ten | GMS | |||
| bending strength | ASTM D-747 | two hundred and sixty | MPa | |||
| Tensile strength fracture point | MD | JIS Z 1702 | forty | MPa | ||
| TD | JIS Z 1702 | thirty-five | MPa | |||
| Thermal performance | vicat softening point | ASTM D-1525 | one hundred | ℃ | ||
| Low temperature embrittlement temperature | ASTM D-746 | <-70 | ℃ | |||
| melting point | DSC method | one hundred and twenty-two | ℃ | |||
| Other performance | Haze | ASTM D-1003 | fourteen | % | ||
| Anti adhesive and smoothing agent | standard | content | ||||
| film thickness | thirty | μ M | ||||