SGP intermediate film 0.89mm film SGPfilm homoshield ionic intermediate film Shandong Chongqing Henan Shandong Henan

Zhejiang Tongdun New Materials Co., Ltd. is located in Tiantai County, Taizhou, Zhejiang Province. It is a technology-based company that produces ion polymer membranes. The company has established long-term cooperative relationships with Zhejiang University of Technology, Wenzhou Research Institute of Chinese Academy of Sciences, etc., and has conducted long-term and in-depth research on the development, detection and application of ionic polymer membranes. The company has a scale of 5000 square meters, and the existing ion polymer membrane production line is designed with an annual production capacity of 1000 tons. It has a good product quality monitoring and testing system, a high-quality R&D and testing team, and strictly controls the quality stability from raw materials to finished products. The company is customer-oriented and quality oriented, providing more efficient products and services to society through continuous deepening research.

Product Introduction

Edge stability refers to the durability of laminated glass edges exposed to atmospheric conditions. PVB adhesive is not resistant to moisture, and it is easy to peel and separate under the action of water vapor. It is required to seal the exposed edges. The Tongdun SGP adhesive has good edge stability, is not sensitive to moisture, and will not open or separate when used under exposed conditions. It can be used with open edges without the need for edge sealing.

• 
  

Product PICTURE

Ordinary PVB laminated glass, especially tempered laminated glass, can undergo significant bending deformation once broken, posing a risk of falling off as a whole. When the glass is horizontally installed on the daylighting roof, the risk is greater, and there have been cases of accidents where the entire piece of glass falls. The SGP intermediate film laminated glass has good integrity, and its tear strength is 5 times that of ordinary PVB intermediate films. Even if the glass breaks, the SGP intermediate film can still bond with the broken glass to form a temporary structure after damage. Its bending deformation is small, and it can also withstand a certain amount of load without the entire piece falling. This greatly improves the safety of glass.

 

 

 

The SGP laminated film itself is colorless and transparent, and has good weather resistance and is not prone to yellowing. The yellowing coefficient of SGP membrane is less than 1.5, while the yellowing coefficient of PVB membrane is 6-12. Therefore, SGP laminated glass can better meet the architectural art requirements of architects. If ultra-white glass (low iron glass) and SGP intermediate film are laminated to form ultra-white laminated glass, the crystal clear optical effect will be achieved.

 

The working performance of several stacked glass sheets depends on the mechanical properties of the intermediate layer (adhesive film). If the shear modulus G and tear strength f of the laminated film are very small (ordinary PVB laminated glass), the middle layer of the laminated glass will experience significant slip when bent, and the glass will slide relative to each other. The laminated film actually does not serve to connect the glass as a whole. If the shear modulus G and tear strength f of the laminated film are very high (SGP laminated glass), the slip of the laminated film is minimal when the laminated glass is bent. At this point, several pieces of glass can work together, as if it were a single piece of glass.

 

 

Comparison of membrane physical parameters

project	Tongdun ionomer membrane	PVB membrane	Testing standards
tensile strength	34Mpa	25Mpa	ASTM D-638
elongation at break	350%	250%	ASTM D-638
density	0.96g/cmthree	1.067/cmthree	ASTM D-792
Transmittance	89%	89%	JC/T2166-2013
Haze	<1%	<1%	JC/T2166-2013
Yellow index	<2	6-12	JC/T2166-2013
Moisture content	<0.1%	0.35% -0.55%	JC/T2166-2013
Coefficient of thermal expansion	100x10-6Mm/mm/℃	155x10-6Mm/mm/℃	ASTM D-696
Thermal deformation temperature	37 ℃	---	ASTM D-648
shear modulus 30 ℃, 3s	140Mpa	1.3Mpa	ISO-6721

 

Product Specification Table

thickness	width	length
0.76mm	Width 2440mm, customized according to customer needs	200 meters
0.89mm	Width 2440mm, customized according to customer needs	200 meters
1.14mm	Width 2440mm, customized according to customer needs	150 meters
1.52mm	Width 2440mm, customized according to customer needs	100 meters

Note: Other thicknesses and sizes can be customized according to actual conditions

Packaging and Storage of Ionic Intermediate Membrane with the Same Shield

Packaging: The inner packaging is vacuum packed with aluminum film, and the outer packaging is packed in wooden boxes. Both the inner and outer packaging are accompanied by a product information certificate.

Storage:It should be stored in a cool and dry place below 30 ℃, avoiding direct sunlight. If the packaging is opened or damaged, it should be placed in a constant temperature dehumidification room with a temperature of 18-25 ℃ and a relative humidity of less than 25% and used as soon as possible.

Transportation:Avoid sunlight, rain, heavy pressure, and severe vibration during transportation.

Shelf life:The normal storage shelf life is two years. After unpacking, it can be stored for three months in a constant temperature dehumidification room with a temperature of 18-25 ℃ and a relative humidity of less than 25%

China is a professional exporter of PVB and SGP film intermediate films, providing transparency, automotive, architecture, color, milky white, porcelain white, Tan, ocean blue, French green, etc

китайский специализированный экспортер полупроводниковых пленок PVB, SGP, поставляющий прозрачные, автомобили, здания, цветные, молочные белила, фарфоровые белила, чайный цвет, морской синий, французский зелёный и т.д.

?? PVB, SGP, etc