Overview
| brand | highest virtue | material quality | 316Ti, S31668, 06Cr17Ni12Mo2Ti |
| specifications | 4mm~920mm~0.5mm~60mm | Processing customization | yes |
| Weighting method | Actual weighing | heat treatment temperature | 1000~1100 ℃ |
| Hot working temperature | 1150-1200 ℃ | density | 7.9 g/cm3 |
| Chromium content | 16.0~18.0 | Nickel content | 10.0-14.0 |
| Molybdenum content | 2.0-3.0 | Titanium content | five × C-0.7 |
| yield strength | ≥ 530 Mpa | tensile strength | ≥ 205 Mpa |
| Elongation rate | ≥ 35% | Corrosion resistance | Good (resistance to intergranular corrosion) |
| Hot working performance | Good (temperature range 900~1200 ℃) | Cold working performance | Good (process characteristics are the same as 316 stainless steel) |
| Welding performance | Good (can use Ao202, Ao207, Ao212) | Executive standards | GB, EN, JIS, ASTM, ASME, GOST |
| Material characteristics | Mainly used for chemical equipment, pipelines, pumps and valves in contact with reducing media | Product Application | Low temperature resistant dilute sulfuric acid, phosphoric acid, and organic acid equipment without intergranular corrosion tendency after welding |